Hydrochloric Acid Corrosion Inhibition of Zn-Al-Cu Alloy by Methyl-Substituted Piperidines
S.S. Mahmoud*
Chemistry Department, University College of Girls for Arts, Science and Education, Ain Shams University, Heliopolis, Cairo, Egypt
Received 4 June 2007; accepted 8 December 2007
Abstract
The corrosion behavior of Zn-Al-Cu alloy was investigated in HCl solution in absence and in presence of different concentrations of inhibitors. The techniques of measurements were: weight loss, linear polarization and galvanic static polarization. It was found that the corrosion rate of this alloy was higher than that of zinc or aluminum. The inhibitors used were: heterocyclic piperidine (PP), 2- methyl piperidine (2mp), 3-methyl piperidine (3mp) and 4- methyl piperidine (4mp). These inhibitors are mixed type and their inhibition efficiency, I%, increases according to the order: 2mp < 3mp < pp < 4mp. The values of activation energy of corrosion were determined in absence and in presence of inhibitors. It was found that the presence of these inhibitors increases the values of activation energy. The adsorption of these inhibitors on the surface of the alloy follows Frumkin’s isotherm.
Keywords: hydrochloric acid, corrosion inhibition, Zn-Al-Cu alloy, methyl-substituted piperidines.
Texto disponível em PDF
Full text only in PDF format
References
1. A.K. Neufeld, I.S. Cole, Proc. Electrochem. Soc. 2000-25 (2001) 444- 452. [ Links ]
2. I.S. Cole, A.K. Neufeld, S.A. Furman, W.J. Miao, Proc. Electrochem. 2000-23 (2001) 284-294.
3. K. Haruhiko, Y. Hayami, A. Masani, Bosei Konri 45-3 (2001) 87- 91.
4. S.F.L. Mertens, E. Temmerman, Corros. Sci. 43-1 (2001) 69-84.
5. J. Tanaka, T. Tamura, T. Narita, Hyomen Gijutsu 51-12 (2000) 1224- 1228.
6. A.R. Moreira, Z. Panossian, J.R. Carvalho, I. Carlos da Silva, EBRATS 10th, Sao Paulo, Brazil, May 22-25 (2000) 617.
7. Y.- Li, Xu-Jun Wei; Fa-lun Ferg, Zhangguo Youse Jinsher Xuebao 11-2 (2001) 248-252.
8. L. Haufei, E.D. Jiashen, Mater- Perform. 40-5 (2001) 32-36.
9. J. Maki, S. Yamaguchi, T. Isaki, M.Kurosaki, Jpn Kokai Tokkyo Koho 316 (2001) 791.
10. J. Zhao, Proc. Corros. Prev. (2000) 612-617.
11. St. Gyurov, N. Guidikova, A. Ilinkina, Tekh. Misul. 33-3 (1996) 86-91 (Bulg).
12. S. Nizoguchi, Y. Nishiki, Yosha Gijutsu 16-3 (1997) 34-40 (Jap).
13. G.A. EL-Mahdy and S.S. Mohmoud, Corros. Sci. 51 (1995) 436.
14. A.G. Gad-Allah, M.M. Hefny, S.A. Salih, M.S. El-Basiouny, Corrosion NACE 45 (1989) 574.
15. M.S. Abdel-Aal, Z.A. Ahmed, M.S. Hassan, J. Appl. Electrochem. 22 (1992) 1104.
16. S.G. Aziz, A.Y. Obaid, A.O. Alyoubi, A.A. Abdel-Fattah, Corros. Preven. Cont. 44 (1997) 179.
17. A. Frignani, G. Trabanelli, F. Zucchi, M. Zucchini, Proc. 5th Europ. Symp. on Corros. Inhibitors, Ferrara, Italy, 1185 (1980).
18. E. Khamis, Corrosion 46-6 (1990) 476.
19. B. Hammouti, A. Aouniti, M. Taleb, M. Brighli, S. Kertit, Corros. Sci. 51 (1995) 411.
20. F. Bentiss, M. Traisnel, M. Lagrenee, Br. Corros. J. 35 (2000) 315.
21. B. Abd-EL Nabey, N. Khalil, A. Mohamed, Surface Technology 24 (1985) 383.
22. S. Kertit, B. Hammouti, Appl. Surf. Sci. 93 (1996) 59.
23. M. Hosseini, S.F.L. Mertens, M. Ghorbani, M.R. Arshad, Materials Chemistry and Physics 78 (2003) 800.
* Corresponding author. E-mail address: drsohairr@hotmail.com.