KORNIENKO, E.; OSSENBRINK, R.    MICHAILOV, V.. Evaluation of corrosion behaviour of organic-coated structured sheet metals. []. , 32, 3, pp.82-86. ISSN 2182-6587.

^len^aIn the present paper the corrosion behaviour of organic-coated structured sheet metals was analysed. These materials are innovative and with three-dimensional geometry. The major advantage of this sheet metal is a higher stiffness in comparison with a smooth sheet. The material was coated by the industrial process of cathodic electrodeposition. The aim of this study is to evaluate the effect of sheet geometry on the corrosion behaviour and the influence of the structuring process on the corrosion properties. For comparison purposes the corrosion resistance of coated smooth sheet metals was determined. The results show that the sheet geometry has no noticeable effect on the corrosion behaviour. The deformation due to the structuring process affects the coating system strongly.^lpt^aNo presente artigo foi analisado o comportamento anticorrosivo de chapas metálicas estruturadas com revestimento orgânico. Estes materiais são inovadores e com geometria tridimensional. A principal vantagem desta chapa metálica é a sua maior rigidez em comparação com a chapa lisa. O material foi revestido pelo processo industrial da electrodeposição catódica. O objectivo deste estudo foi a avaliação do efeito da geometria da chapa no comportamento corrosivo e a influência do processo estruturante nas propriedades corrosivas. Como referência foi determinada a resistência à corrosão de chapas metálicas lisas revestidas. Os resultados revelaram que a geometria da chapa não teve efeito perceptível no comportamento corrosivo. A deformação devido ao processo de estruturação afecta fortemente o sistema de revestimento.

: .

        · | |     ·     · ( pdf )