MARTINS, J. I.    BAZZAOUI, M.. Comparative study of polypyrrole films electrosynthesized on zinc surfaces from organic and aqueous solutions. []. , 34, 1, pp.5-11. ISSN 2182-6587.

^len^aHomogeneous and adherent polypyrrole coatings have been achieved on zinc electrodes previously treated with an aqueous solution of sulfide in the acetonitrile medium with tetraethylammonium p-toluene sulfonate, and in the tartrate aqueous medium without any chemical or electrochemical pretreatment of the working electrode. The XPS and AES analysis showed that the dissolution of the working electrodes is inhibited in the first polarization medium by the oxide and zinc sulfide formed on the surface during the pretreatment in 0.2 M Na₂S after 12 h, or by the zinc tartrate film developed through the electrode polarization in the second. The adherence, compactness and corrosion performance in 0.1 M HCl of the polypyrrole coatings from the tartrate solution are higher than those obtained from acetonitrile medium.^lpt^aRevestimentos de polipirrol homogéneos e aderentes foram obtidos sobre eléctrodos de zinco previamente tratados numa solução aquosa de sulfureto em meio de acetonitrilo com p-tolueno-sulfonato de tetraetilamónio, e em meio aquoso de tartarato sem qualquer pré-tratamento químico ou electroquímico do eléctrodo de trabalho. As análises por XPS e AES mostraram que a dissolução dos eléctrodos de trabalho é inibida no primeiro meio de polarização pelo óxido e sulfureto de zinco formados sobre a superfície durante o pré-tratamento em Na₂S 0,2 M após 12 h, ou pelo filme de tartarato de zinco desenvolvido sobre o eléctrodo no segundo meio de polarização. A adesão, compacidade e comportamento à corrosão em HCl 0,1 M dos revestimentos de polipirrol obtidos a partir da solução de tartarato são melhores do que os provenientes do meio de acetonitrilo.

: .

        · | |     ·     · ( pdf )