ERAKHRUMEN, Andrew A.    OGUNSANWO, Olukayode Y.. Influence of Neem Seed Oil-Treatment on Static Bending Strength Properties of Wild Grown Split-Bamboo (Bambusa vulgaris Schrad.) in South-West Nigeria. []. , 18, 2, pp.167-177. ISSN 0870-6352.

^len^aThis paper intends to contribute to the efforts aimed at achieving sustainable environmentally benign methods of treating and preserving lignocellulosic materials. For this study, split-bamboo samples, with mean specific gravity of 0.89 and conditioned in the laboratory to 11.76% moisture content were treated, at two different temperature regimes, with mechanically extracted neem seed oil. Selected mechanical properties for the oil-treated and untreated bamboo samples were determined in conformity with modified ASTM D 143-83. Results showed that mean values for moduli of rupture and elasticity (MOR and MOE) for static bending strength test were lowest in samples soaked in hot oil at 60ºC for 4 hours but higher in samples soaked in oil at room temperature of 25±2ºC for 24 hours, with control samples possessing higher values than those for the oil-treated samples. One way analysis of variance also revealed statistical significant variation in the data obtained for MOR and MOE at 5% significance level. Fishers Least Significant Difference was used as a follow-up test to compare means, also at 5% significance level.^lpt^aEste estudo pretendeu contribuir para o desenvolvimento de métodos ambientalmente benignos para o tratamento e preservação dos materiais lenhocelulósicos. Com este objectivo submeteram-se amostras de bambu de densidade média de 0,89, condicionadas em laboratório para obtenção de humidade de 11,76%, a tratamento com óleo extraído mecanicamente de sementes de Azadiracta indica sob dois regimes de temperatura. As propriedades mecânicas para caracterização dos provetes tratados e não tratados com óleo foram determinadas em conformidade com a norma ASTM D 143-83. Os valores médios dos módulos de ruptura e elasticidade (MOR e MOE) dos testes de resistência à flexão estática foram mais baixos nas amostras mergulhadas em óleo quente a 60ºC durante 4 horas, e mais elevados em amostras mergulhadas em óleo à temperatura ambiente de 25±2ºC durante 24 horas, sucedendo que os valores dos provetes testemunha foram mais elevados que os correspondentes aos provetes tratados com óleo. A análise de variância univariada também revelou diferenças estatisticamente significativas nos dados obtidos para MOR e MOE, para um nível de significância de 5%. A comparação das médias dos resultados foi realizada com recurso ao teste de diferença de médias de Fisher.^lfr^aCe travail a eu comme objectif de contribuer aux efforts de développement de méthodes bénignes pour l'environnement, pour traiter et préserver les matériaux lignocellulosiques. Pour cette étude, des échantillons de bambou, ayant une densité moyenne de 0.89 et conditionnés en laboratoire jusqu'à l'obtention d'une teneur en eau de 11.76%, ont été traités, à deux régimes différents de température, avec l'huile de graines de neem mécaniquement extraite. Les propriétés mécaniques choisies pour les échantillons en bambou huile-traitée et non traitée étaient déterminées conformément à ASTM modifié D 143-83. Les résultats ont prouvé que les valeurs moyennes pour des modules de la rupture et de l'élasticité (MOR et MOE) pour l'essai statique de résistance à la flexion étaient les plus basses dans les échantillons imbibés dans de l'huile chaude à 60ºC pendant 4 heures, mais plus élevées dans les échantillons imbibés dans de l'huile à la température ambiante de 25±2ºC pendant 24 heures, les échantillons témoins possédant des valeurs plus élevées que ceux des échantillons huile-traités. L'analyse de la variance à sens unique a aussi indiqué la variation statistiquement significative des données obtenues pour MOR et MOE au niveau de signification de 5%. Le test de «la moindre différence significative» de Fisher a été employé comme essai de suivi pour comparer les moyennes, également au niveau de signification de 5%.

: .

        · | | |     ·     · ( pdf )