LOPES, Julio C. O.. Os aços Maraging. []. , 19, 1-2, pp.41-44. ISSN 0870-8312.

^len^aThis paper reports a developments and recent researches of Maraging steel . The mechanical proprieties of this class of steel is very interesting for aeronautical applications  speciality for toughness and strength resistence.  The martensitic transformation allow a high density of dislocations in a CBC structure , and this dislocation, will be a preferred site for precipitation during the aging treatment. The precipitation hardening is responsible about fifty percent of total hardening in this steel grade. For this reason, the real studies are concentrates in the precipitation phenomena. New types of alloys are added to modify the precipitation effect.^lpt^aEste artigo apresenta informações sobre o desenvolvimento e pesquisas realizadas sobre os aços Maraging. Neste tipo de aço, as propriedades mecânicas são muito interessantes para a aplicação aeronáutica, especialmente nas propriedades de resistência mecânica e tenacidade. Nestes aços , a transformação martensítica produz uma martensita de estrutura cúbica de corpo centrado com elevada densidade de discordâncias. Estas discordâncias atuam como sítios nucleadores para a precipitação de compostos intermetálicos que ocorre durante o envelhecimento. O endurecimento por precipitação nestes aços é responsável por aproximadamente cinqüenta porcento do endurecimento total apresentado por este tipo de aço, e é por este motivo que os eforços.

: .

        · | |     · |     · ( pdf )