SILVA, R. P. et al. Ni-co alloys electrodeposited in stainless steel for supercapacitors electrodes. []. , 32, 2, pp.37-41. ISSN 2182-6587.

^len^aThe development of electric energy storage devices with high power density has become one of the most challenging research areas in a wide range of applications. In this context, electrochemical supercapacitors are attracting great attention due to their high potential density, fast charge-discharge cycles and high number of life cycles. In the present work, Ni-Co nanostructured films were produced by electrodeposition technique in order to form a porous dendritic structure with enhanced surface area. The electrochemical behaviour of the deposited films was studied by charge-discharge experiments. The Ni-Co dendritic films electrodeposited at current densities i₁ = -4 mA cm^-2 and i₂ = -30 mA cm^-2 display a specific capacitance of 215 F g^-1. The capacitance loss is about 33 % after 6000 charge-discharge cycles.^lpt^aO desenvolvimento de dispositivos de armazenagem de energia com elevada densidade de potência tornou-se numa área de investigação de grande interesse para um vasto campo de aplicações. Os supercondensadores eletroquímicos para além de elevada densidade de potência possuem tempos de carga e descarga reduzidos e elevado número de ciclos de vida. No presente trabalho, produziram-se filmes de Ni-Co nanoestruturados por eletrodeposição com uma estrutura dendrítica de elevada área superficial. O comportamento eletroquímico dos filmes depositados foi estudado através de ensaios de carga-descarga. Os filmes depositados a densidades de corrente i₁= -4 mA cm^-2 e i₂= -30 mA cm^-2 apresentaram um valor de capacidade específica de 215 F g^-1. A perda de capacidade é de 33 % ao fim de 6000 ciclos de carga descarga.

: .

        · | |     ·     · ( pdf )