EVARISTO, M.; NOSSA, A.  y  CAVALEIRO, A.. Tribological behaviour of reactive and co-sputtered W-S-C coatings. C.Tecn. Mat. [online]. 2006, vol.18, n.1-2, pp.21-26. ISSN 0870-8312.

W-C-S films were deposited either by a reactive process in an Ar+CH₄ atmosphere or by co-sputtering WS₂ and C targets. The films were characterized concerning their chemical composition and mechanical properties. The results showed that the films, in both systems, have similar properties. Co-sputtered films are amorphous, whereas in the reactive process a gradual l oss of cristallinity is observed with the increase of C content in the films. The hardness and the adhesion are similar for both systems. The increase of C alloying to the films led to the improvement of both their hardness and adhesion. The tribological performance of the coatings was tested by ball-on-disk. The films deposited by co-sputtering present better results than the reactive deposited ones. With the increase of C content in these coatings an increase of the wear resistance is observed, reaching in the best case a wear coefficient of 3.1×10^-16 m³/N×m. In the films deposited by reactive process, low wear coefficients can also be reached but no regular trend with increasing C contents can be observed.

Palabras clave : Tungsten disulfide; WS₂; Friction coefficient; Wear coefficient; Self-lubricant.

        · texto en Inglés     · Inglés ( pdf )