SALIH, S.A.; MAZHAR, A.A.  y  MAHANNY, H.. The Effect of Sour Gases and Some Anions on the Corrosion Behavior of Carbon Steel. Port. Electrochim. Acta [online]. 2004, vol.22, n.3, pp.205-225. ISSN 0872-1904.

The effect of the presence of CO₂ and H₂S in the well water used in the petroleum plant  on corrosion of carbon steel has been tested using impedance measurements. Carbon dioxide leads to decrease in the resistivity of the film developed on the metallic surface, while the effect of hydrogen sulfide is less pronounced. Scanning electron micrographs have shown that corrosion products cover only small part of metallic surface in water containing CO₂. Studies under polarization conditions will allow concluding that the dissolved gases in the well water reduce the ability of the film to protect the metal against corrosion. The influence of the oxoanions and halide ions on the corrosion rate of steel has also been analyzed.

Palabras clave : corrosion; sour gases; carbon steel; petroleum plant.