SANDOVAL-JABALERA, R. et al. Corrosion behaviour of 1018, 410 and 800 steels in synthetic wastewater . Port. Electrochim. Acta [online]. 2006, vol.24, n.4, pp.393-404. ISSN 0872-1904.

The corrosion behaviour of 1018, 410 and 800 steels exposed to synthetic wastewater has been studied using linear polarization resistance (LPR), cyclic potentiodynamic curves (CPC), electrochemical noise (EN), and electrochemical impedance spectroscopy (EIS) tests. The conditions were: biochemical oxygen demand (BOD) of 776 ppm, a chemical oxygen demand (COD) of 1293 ppm, pH = 8 and the cell temperature was 24 °C. From the CPC and EN results, no localized corrosion was found for the stainless steels. However, the reverse was true for the 1018 steel. The EIS results showed that different corrosion mechanism occurred for the carbon steel compared with the stainless steels. This shows that the corrosion mechanism strongly depends on the type of steel. Overall, the 1018 steel exhibited the highest corrosion rate, followed by the 410 alloy. The highest corrosion resistance was achieved by the 800 alloy. In addition, SEM analyses were carried out to explain the experimental findings.

Palabras clave : carbon steel; electrochemical behaviour; stainless steels; synthetic wastewater.

        · texto en Inglés     · Inglés ( pdf )