JEYARAJ, S.; ARULSHRI, K.P.  e  SIVASAKTHIVEL, P.S.. Effects of Process Parameters on Microhardness of Electrodeposited Ni-Al Composite Coating Using Taguchi Method. Port. Electrochim. Acta [online]. 2015, vol.33, n.5, pp.249-264. ISSN 0872-1904.  https://doi.org/10.4152/pea.201505249.

This paper aims at investigating the influence of process parameters on micro hardness of metal matrix / material particle coated steel plates. The electro deposition parameters such as current density, pH of bath, bath temperature, Al particles concentration in the bath and agitation speed were considered for this study. Nickel matrix / aluminum particle composite coatings were prepared from a Watt's bath by electro-codeposition method. The Taguchi method was used to establish the relationship between the process parameter and response variable, micro hardness of the coated plate. L27 Taguchi orthogonal design was employed for conducting the experiments. The micro-hardness of the deposits was examined using a Vickers micro-hardness tester with the payload of 100 g for 10 sec of indentation period. Signal-to-noise ratio and analysis of variance were employed to determine the significance of the process parameter. The surface morphologies of coating and vol. % of Al particles in deposits were analyzed using optical and scanning electron microscope observations.

Palavras-chave : Ni-Al composite coating; Orthogonal Array; Micro hardness; Taguchi's approach; S-N ratio.