Electrode Passivation in the Electrocoagulation Process

 

Gilberto B. Rios,* Facundo Almeraya, Ma. Teresa A. Herrera

 

Centro de Investigación en Materiales Avanzados Miguel de Cervantes 120. Complejo Ind. Chihuahua. CP 31109, Chihuahua, Chihuahua. México.

 

Received 15 February 2004; accepted in revised form 12 December 2004

 

 

Abstract

One of the main limiting factors of the electrocoagulation, as a process of treatment for remotion of contaminants from residual waters, is not knowing the degree of interaction of some variables which could significantly affect the system. The electrode passivation is one of them once its presence limits the emission of metallic ions and consequently the treatment time is increased as well as cost, and remotion efficiency is decreased. In the present work potentiodynamic and potentiostatic curves were used to observe the behaviour of current density vs. pH, electrical conductivity, distance between electrodes, auxiliary electrode area and applied potential difference. We found out that all the above variables influence the current density, that passivation is at 50 mV, independently of all the other variables, and that at 2000 mV, only is observed when pH = 2 and high electrical conductivities.

Keywords: potentiostatic and potentiodynamic curves, current density, residual water.

 

Pasivación de los Electrodos en el Proceso de Electrocoagulación

 

Resumen

Una de las principales limitantes de la electrocoagulación como proceso de tratamiento para remoción de contaminantes del agua residual, es el desconocimiento del grado de interacción de algunas variables que podrían influir significativamente al sistema, de las cuales, la pasivación de los electrodos es una de ellas, debido a que su presencia limita la emisión de iones metálicos y por consecuencia se incrementan los tiempos de tratamiento, costos de operación y se reduce la eficiencia de remoción. En el presente estudio se emplearon curvas potenciodinámicas y potenciostáticas para observar el comportamiento de la densidad de corriente ante el efecto del pH, conductividad eléctrica, distancia entre electrodos, área de electrodo auxiliar y la diferencia de potencial aplicado, determinándose que todas las variables tienen influencia en la densidad de corriente; que la pasivación se presenta a potenciales de 50 mV, independientemente del resto de las variables, y que a potenciales de 2000 mV, sólo se presenta cuando se tiene pH 2 y altas conductividades eléctricas.

Palabras clave: curvas potenciodinámicas y potenciostáticas, densidad de corriente, agua residual.

 

 

Texto completo disponível em PDF

Full text only in PDF format

 

 

Reference

 

1.       L. Joffe and L. Kniper, Industrial Waste Water 20 (2000) 1-6.        [ Links ]

2.       F. Chuanping, S. Norio, Sh. Satoru, M. Takaaki, J. Haz. Mater. B 103 (2003) 65-78.         [ Links ]

3.       M.Y. Mollah, R. Shennach, J.R. Praga, D.L. Cocke, J. Haz. Mater. B 84 (2001) 29-41.        [ Links ]

4.       C. Tsouris, D.W. DePaoli, J.T. Shor,  M.Z.-C. Hu, T.Y. Ying, Colloids Surf. Phys. Eng. Asp. 177 (2001) 223-233.        [ Links ]

5.       N. Mameri, H. Lounici, D. Belhocine, H. Grib, D.L. Piron, Y. Yahiat, Separat. Purif. Tech. 24 (2001) 113-119.        [ Links ]

6.       U.R. Evans, “Corrosiones metálicas”. Editoriales Reverte, S.A de C.V. (1987). pp. 68-79.        [ Links ]

7.       F.J.A. González, “Control de la corrosión. Estudio y medida por técnicas electroquímicas”. Editorial C.S.I.C. España. (1989). pp. 165-193.        [ Links ]

8.       X. Chen, G. Chen and P.L. Yue, Separat. Purif. Tech. 19 (2000) 65-76.         [ Links ]

9.       G. Chen, X. Chen, P.L. Yue, J. Env. Eng. 126-9 (2000) 858-863.        [ Links ]

 

* Corresponding author. E-mail address: gilberto.badillo@cimav.edu.mx